GC Initial® IQ Lustre Pastes NF
GC Initial IQ Lustre Pastes NF are 3-dimensional ceramic pastes developed to create color depth and life-like translucency with a single paint on application. Thanks to the “New Formula” (NF), you can really bring your crowns and bridges to life with this dedicated Lustre Paste Set, an optimal match to both “low” and “high” CTE ceramics. The product is available in a ready to use consistency. The GC Initial IQ Lustre Pastes NF are based on fine ceramic particles and can be applied in a thicker layer where they exhibit unsurpassed vitality and a very natural glaze to your restorations.
- With an optimal match to both “low” & “high” CTE range, they are compatible to almost all types of dental ceramic
- They are based on fine ceramic particles, allowing a thicker application compared to conventional stains & glazes
- Due to the unique paste medium, it has a fine thixotropic property for easy and exact applications
- They are low fusing, ceramic pastes that do not wear like some stains, glazes, or surface protectants
- Just one dedicated kit for all different indications for the complete GC Initial ceramic range
- Available in a ready to use consistency (1 x Neutral, 1 x Value, 4 x Body Shades, 10 x Enamel Effect Shades)
- Just one kit compatible with the complete GC Initial ceramic range (CTE – Range between 6,9 and 13,3)
- Available in a ready to use jars for a more convenient application
- Diluting and Refresh liquids to keep the optimal consistency until the end
- Improved pastes with a finer thixotropic property for easy and precise application
- 2 additional colours available: Olive, for greenish effects and Value to modify the brightness
SKU: n/a -
Ceramics, Laboratory, Laboratory Material
GC Initial® LiSi Press
GC Initial LiSi Press is a high-strength lithium disilicate ingot with proprietary HDM (High Density Micronization) technology that equally disperses micro-crystals—rather than traditional larger-size crystals—to fill the entire glass matrix, resulting in excellent physical properties and aesthetics. It has a biaxial flexural strength of >500MPa and virtually no reaction layer when divested. The material is wear resistant, stable after multiple firings and optimized for use with GC Initial® LiSi veneering ceramic and GC Initial® IQ Lustre Pastes NF.
- Wear resistant
- Material is stable after multiple firings
- Virtually no reaction layer when divested
- Excellent physical properties and aesthetics
- Biaxial flexural strength of >500 MPa with HDM Technology
- Optimized for use with GC Initial® LiSi veneering ceramic and GC Initial® IQ Lustre Pastes NF